The structural transition of AIN nanocrystals and nanowires were investigated simultaneously under pressures up to 37.2 GPa by in situ angle dispersive high-pressure x-ray diffraction using synchrotron radiation source and a single diamond anvil cell. The size of hexagonal AIN nanocrystals and the diameter of nanowires are 45 nm on average. A pressure-induced wurtzite to rocksalt phase transition starts at 21.5 GPa and completes at 27.8 GPa for the nanocrystals and nanowires, respectively. The high-pressure behaviors of AlN nanocrystals the same as the AIN nanowires might arise from the similar size and diameter in nanocrystals and nanowires. Hexagonal AIN nanocrystals (45 nm) display an apparent volumetric contraction as compared to the AlN nanocrystals (10 nm) which might induce the difference of transition pressure.