Crystallographic analysis of nano-structured bainitic steels

A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200 and 350°C bainitic transformation temperatures. The microstructure was consisted of bainitic ferrite lath and retained austenite for both heat treatment conditions. The crystallographic analysis revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with their parent austenite. The isothermal bainite transformation temperature has a significant effect on the retained austenite characteristics and the variant selection of the bainitic ferrite laths. In general, a decrease in the isothennal bainite transformation temperature refined the bainitic structure and weakened the variant selection.