Corrosion of porous Ti35Zr28Nb in Hanks’ solution and 3.5 wt% NaCl
Version 2 2024-06-06, 09:16Version 2 2024-06-06, 09:16
Version 1 2019-03-14, 12:41Version 1 2019-03-14, 12:41
journal contribution
posted on 2024-06-06, 09:16authored byM Heywood, Z Shi, Y Li, C Wen, J Kanwar, Y Xiao, A Atrens
The present research examined the corrosion and crevice corrosion behavior of porous specimens of Ti35Zr28Nb and CP Ti in Hanks’ solution at 37 °C and in 3.5 wt% NaCl at 95 °C. The following conclusions can be drawn. There was no crevice corrosion for porous specimens of Ti35Zr28Nb and CP Ti in Hanks’ solution at 37 °C and in 3.5 wt% NaCl at 95 °C. Both alloys had low corrosion rates in both solutions, and both alloys were passive in both solutions.