Effect of twinning on microstructural evolution during dynamic recrystallisation of hot deformed as-cast austenitic stainless steel

Version 2 2024-06-03, 11:00
Version 1 2015-09-07, 12:26
journal contribution
posted on 2024-06-03, 11:00 authored by A Guria, GK Mandal, Peter HodgsonPeter Hodgson, JH Beynon, SG Chowdhury
An as-cast austenitic stainless steel was hot deformed at 1173 K, 1223 K, and 1373 K (900 °C, 950 °C, and 1100 °C) to a strain of 1 with a strain rate of 0.5 or 5 s−1. The recrystallised fraction is observed to be dependent on dynamic recrystallisation (DRX). DRX grains nucleated at the initial stages of recrystallization have similar orientation to that of the deformed grains. With increasing deformation, Cube texture dominates, mainly due to multiple twinning and grain rotation during deformation.

History

Journal

Metallurgical and materials transactions a

Volume

46

Pagination

4423-4428

Location

New York, N.Y.

ISSN

1073-5623

Language

eng

Publication classification

C Journal article, C1 Refereed article in a scholarly journal

Copyright notice

2015, Springer

Issue

10

Publisher

Springer