Extrusion properties of a Zr-based bulk metallic glass

The extrusion behavior of Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5 metallic glasses in the supercooled liquid region was investigated. Good extrusion formability was observed under low strain rates at temperatures higher than 395 °C. The metallic glasses were fully extruded without crystallization and failure within the range of T=395–415 °C under strain rates from 5×10⁻³ s⁻¹ to 5×10⁻² s⁻¹, and the deformation behavior of the metallic glasses during the extrusion was found to be in a Newtonian viscous flow mode by a strain rate sensitivity of 1.0.