Mechanical twinning and texture evolution during asymmetric warm rolling of a high manganese steel

journal contribution
posted on 2019-09-09, 00:00 authored by F Brasche, Jiangting Wang, Ilana Timokhina, C Haase, Rimma LapovokRimma Lapovok, D A Molodov
© 2019 Elsevier B.V. Asymmetric rolling is known to strongly refine the microstructure of metallic alloys due to an additional shear strain component introduced to the material, as compared to symmetric rolling. Additionally, the rolling temperature significantly influences the stacking fault energy (SFE) and thus, may be used to control the activation/suppression of the deformation mechanisms, such as deformation twinning. In the present study, asymmetric rolling at temperatures ranging from room temperature to 400 °C was applied to a high-manganese Twinning-Induced Plasticity (TWIP) steel in order to tailor the yield strength- ductility combination. Microstructure and texture evolution were investigated by transmission electron microscopy (TEM), electron backscatter diffraction (EBSD) and x-ray diffraction (XRD) in order to gain a detailed insight into the active deformation mechanisms and their effect on the mechanical properties. The combination of applied asymmetry and rolling at elevated temperatures resulted in a high yield strength (1047 MPa) due to a high density of dislocations and stacking faults on the one hand and a reasonably high ductility (30%) on the other hand. The latter was achieved by partial suppression of deformation twinning during warm rolling and subsequent activation of twinning during room temperature tensile testing. The suppression of twinning at elevated temperatures was most effective at low rolling degrees and resulted in a weak transition texture with characteristics of both Cu-type and Brass-type texture. In turn, at higher rolling degrees, where twinning was only partially suppressed, a weak Brass-type texture was developed.

History

Journal

Materials Science and Engineering A

Volume

764

Article number

138183

Pagination

1 - 8

Publisher

Elsevier

Location

Amsterdam, The Netherlands

ISSN

0921-5093

Language

eng

Publication classification

C1 Refereed article in a scholarly journal