Na partitioning during thermomechanical processing of an Mg-Sn-Zn-Na alloy

Microstructural characterization was used to examine the changes that occur in an Mg-6Sn-5Zn-0.3Na alloy from casting to extrusion at either 623 K or 723 K (350 _C or 450 _C) followed by artificial aging at 473 K (200 _C). In particular, the partitioning of Na was examined at each step using STEM-EDS mapping. Na atoms were found to preferentially partition to the Mg-Zn phase when present. After extrusion, when no Mg-Zn was observed, the spherical Mg2Sn particles were found to be enriched in Na, particularly at the higher extrusion temperature. Artificial aging following extrusion resulted in a change in Na partitioning, and a coarse distribution of Mg-Zn precipitate rods. Na microadditions led to a high as-extruded hardness, but a significant tension–compression yield asymmetry was still observed at room temperature. The compressive yield strength was found to decrease significantly after 1000 hours of aging.