Phosphorus-containing diamine for flame retardancy of high functionality epoxy resins. Part II. The thermal and mechanical properties of mixed amine systems

journal contribution
posted on 08.03.2006, 00:00 authored by W Liu, Russell VarleyRussell Varley, G P Simon
Bis(4-aminophenoxy)phenyl phosphonate (BAPP) was used in various ratios in combination with diethyltoluenediamine (DETDA) to investigate the effect of increasing phosphorous addition upon the thermal and mechanical properties of diglycidyl ether of bisphenol A (DGEBA) and tetra glycidyl dimethylenedianiline (TGDDM) based epoxy networks. Increasing phosphorous content was shown to decrease the temperature of the initial onset of degradation, while the char yield at 540 °C increased in both the nitrogen and air atmosphere. At 700 °C, however, the char formation was shown to be dependent upon the atmosphere with an oxidative environment promoting further chain scission, while a non-oxidative environment promoted char formation through crosslinking reactions. Increasing phosphorous content was found to produce only modest decreases in the glass transition temperatures, while no significant deleterious effects upon the mechanical and physical properties such as flexural properties and CTE were observed.

History

Journal

Polymer

Volume

47

Issue

6

Pagination

2091 - 2098

Publisher

Elsevier

Location

Amsterdam, The Netherlands

ISSN

0032-3861

Language

eng

Publication classification

C1.1 Refereed article in a scholarly journal

Copyright notice

2006, Elsevier