Poly(ethylene oxide carbonates) solid polymer electrolytes for lithium batteries
journal contributionposted on 2018-02-20, 00:00 authored by L Meabe, T V Huynh, N Lago, H Sardon, C Li, Luke O'DellLuke O'Dell, M Armand, Maria ForsythMaria Forsyth, D Mecerreyes
Poly(ethylene oxide) (PEO) is the gold standard matrix for polymer electrolytes used in actual all-solid lithium batteries. However, PEO solid polymer electrolytes show some limitations; such as relatively low ionic conductivity and lithium transference number resulting in the actual polymer-lithium batteries operating at 70 °C. In the last years, polycarbonates (PC) have been presented as an alternative polymer matrix with superior ionic conductivity for solid batteries which may work at room temperature. In this article we systematically investigated the properties of new polymers which combine varying composition of both ethylene oxide and carbonate groups. A series of poly(ethylene oxide carbonates) (PEO-PCs) have been synthesized by polycondensation between different ethylene oxide diols and dimethyl carbonate. As a result, eight new PEO-PCs with number of ethylene oxide units ranging from 2 to 45 between carbonate groups were synthesized and characterized in terms of physico-chemical properties (Tmand Tg). These PEO2-45-PC were formulated as solid polymer electrolytes (SPE) by adding different amounts of bis(trifluoromethane)sulfonimide lithium salt. The effect of the SPE composition (ethylene oxide/carbonate ratio, salt content) on the ionic conductivity and thermal properties (glass transition temperature and melting temperature) was investigated. The optimum SPEs showing the lowest glass transition temperature led to highest ionic conductivity value of 3.7·10−5S cm−1at room temperature. FTIR spectra revealed the coordination between the carbonate groups in the polymer chain and the lithium salt.7Li-19F NMR analysis T1relaxation and diffusion coefficients measurements indicated local dynamics that correlates with the general conductivity behaviour.
Pagination367 - 375
LocationAmsterdam, The Netherlands
Publication classificationC1 Refereed article in a scholarly journal
Copyright notice2018, Elsevier Ltd.
CategoriesNo categories selected
Solid polymer electrolytesPolycarbonatepoly(ethylene oxide)Amorphous polymerIonic conductivity7 Li-19F NMR studiesLocal dynamicsActivation energyDiffusion coefficientScience & TechnologyPhysical SciencesElectrochemistryLi-7-F-19 NMR studiesALIPHATIC POLYCARBONATESTRANSPORT-PROPERTIESAMBIENT-TEMPERATUREMOLECULAR-WEIGHTCONDUCTIVITYCOPOLYMERSFUTUREISSUES