Super Water Repellent Fabrics Produced by Silica Nanoparticle-containing Coating

Version 2 2024-06-13, 06:44
Version 1 2022-11-30, 01:35
journal contribution
posted on 2024-06-13, 06:44 authored by H Wang, J Ding, T Lin, X Wang
In this paper, we report on superhydrophobic fabrics (polyester, wool and cotton) produced by a wet-chemical coating technique. The coating solutions were synthesized by the co-hydrolysis of two silane precursors, tetraethyl orthosilicate (TEOS) and an alkylsilane, in an alkaline condition. Without any purification, the as-hydrolyzed solutions were directly used to treat fabrics, and the treated fabrics had water contact angles (CA) as high as 170° and sliding angles (SA) as low as 5°. Three alkylsilanes have been used for the synthesis of the coating solutions, and all contain three hydrolysable alkoxyl groups and one non-hydrolysable alkyl, but with different chain lengths (C1, C8 and C16). It was found that the CA value increased with an increase in the alkyl chain length, while the SA showed a reverse trend. When the functional group had a C16 alkyl, the treated fabric surfaces were highly superhydrophobic, with the CA not being affected much by the fabric type, while theSA values were slightly affected by the original wettability of the fabric substrates. The superhydrophobic feature was attributed to a highly rough surface formed by the particulate coating. Aside from the superhydrophobicity, the influence of the coating on the fabric softness was also examined.

History

Journal

Research Journal of Textile and Apparel

Volume

14

Pagination

30-37

ISSN

1560-6074

eISSN

2515-8090

Language

en

Publication classification

C1.1 Refereed article in a scholarly journal

Issue

2

Publisher

Emerald

Usage metrics

    Research Publications

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC