Unexpectedly high piezoelectricity of electrospun polyacrylonitrile nanofiber membranes
journal contribution
posted on 2019-02-01, 00:00 authored by W Wang, Y Zheng, X Jin, Y Sun, B Lu, Hong Wang, Jian Fang, Hao Shao, Tong Lin© 2018 Elsevier Ltd Polyvinylidene fluoride (PVDF) and its co-polymers are among the best piezoelectric polymer materials owing to the large piezoelectric coefficient and mechanical properties. Processing PVDF polymers into fibrous membranes through electrospinning can largely increase the piezoelectricity. In contrast, polyacrylonitrile (PAN), an amorphous polymer, is known to have a much lower piezoelectricity than PVDF. Herein, we report an unusually-high piezoelectric feature of electrospun PAN nanofiber membranes. When a small piece of PAN nanofiber nonwoven membrane (e.g. 5 cm 2 ) was subjected to compressive impact, it can generate up to 2.0 V of voltage, the electrical outputs of which are even higher than that of PVDF nanofiber membranes at the same condition. Such unexpected piezoelectric properties were found to originate from the high content of planar Sawtooth PAN conformation within nanofibers. Electric charges in PAN nanofibers also contributed to the energy conversion. The energy conversion capability can be further enhanced by increasing fiber orientation within fibrous membrane. Also, the working area and thickness of nanofibrous membranes as well as impact conditions influenced piezoelectric outputs. The energy generated is usable and can power commercial LEDs. These unexpected discovery may inspire to develop novel piezoelectric materials and devices.
History
Journal
Nano energyVolume
56Pagination
588 - 594Publisher
ElsevierLocation
Amsterdam, The NetherlandsPublisher DOI
ISSN
2211-2855Language
engPublication classification
C1 Refereed article in a scholarly journalCopyright notice
2018, ElsevierUsage metrics
Categories
No categories selectedKeywords
Licence
Exports
RefWorksRefWorks
BibTeXBibTeX
Ref. managerRef. manager
EndnoteEndnote
DataCiteDataCite
NLMNLM
DCDC