Evolution of hot working stress and microstructure of Mg-3Al-1Zn

thesis
posted on 2004-01-01, 00:00 authored by A Beer
The deformation behaviour of magnesium alloy AZ31 was examined. The work found that dynamic recrystallisation operates during hot deformation. The influence that different process variables have on this mechanism were quantified. The optimisation of dynamic recrystallisation allows magnesium alloys to be formed into products more easily whilst developing enhanced final properties.

History

Pagination

xvii, 220 leaves : ill. ; 30 cm.

Material type

thesis

Resource type

thesis

Language

eng

Notes

Thesis (Ph.D.)--Deakin University, Victoria, 2004.

Degree name

Ph.D.

Thesis faculty

Faculty of Science

Thesis school

Engineering and Built Environment

Usage metrics

    Theses

    Categories

    No categories selected

    Keywords

    Magnesium alloys - MetallurgyMagnesium alloys - Hot workingDeformations (Mechanics)Recrystallization (Metallurgy)Microstructure

    Licence

    All Rights Reserved

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC