Electrospun tin oxide nanofibers with different precursor solution

Bai, Xue, Jia, Di, Cheng, Bowen, Kang, Weimin and Li, Quanxiang 2011, Electrospun tin oxide nanofibers with different precursor solution, Materials Science Forum, vol. 675 677, pp. 275-278, doi: 10.4028/www.scientific.net/MSF.675-677.275.

Attached Files
Name Description MIMEType Size Downloads

Title Electrospun tin oxide nanofibers with different precursor solution
Author(s) Bai, Xue
Jia, Di
Cheng, Bowen
Kang, Weimin
Li, QuanxiangORCID iD for Li, Quanxiang orcid.org/0000-0002-0190-1930
Journal name Materials Science Forum
Volume number 675 677
Start page 275
End page 278
Total pages 4
Publisher Trans Tech Publications, Ltd.
Publication date 2011-01-01
ISSN 0255-5476
Summary In this paper, electrospinning method was adopted to prepare tin oxide nanofibers membrane with three kinds of novel precursor solution PVP/C12H24O4Sn, PVP/ C4H10OSn and PVP/SnCl4. The morphology, surface element, thermal analysis and crystal structure of the fibers membrane were investigated by SEM, EDS, TG-DTA and XRD. The results showed that the organic/inorganic hybrid nanofibers with an average diameter of 300~700 nm can be obtained by electrospinning. But after calcined at 600°C, the loose and porous tin oxide nanofibers membrane with an average diameter of 100~250 nm can be obtained only by using PVP/SnCl4 as preceusor solution, moreover, it showed good fiber forming property. From XRD spectra, it was found that the rutile structure tin oxide finally obtained without other crystalline forms.
Language eng
DOI 10.4028/www.scientific.net/MSF.675-677.275
Indigenous content off
Field of Research 0306 Physical Chemistry (incl. Structural)
0912 Materials Engineering
HERDC Research category C1.1 Refereed article in a scholarly journal
Persistent URL http://hdl.handle.net/10536/DRO/DU:30124899

Document type: Journal Article
Collections: Institute for Frontier Materials
GTP Research
Connect to link resolver
Unless expressly stated otherwise, the copyright for items in DRO is owned by the author, with all rights reserved.

Version Filter Type
Citation counts: TR Web of Science Citation Count  Cited 0 times in TR Web of Science
Scopus Citation Count Cited 0 times in Scopus
Google Scholar Search Google Scholar
Access Statistics: 102 Abstract Views, 0 File Downloads  -  Detailed Statistics
Created: Thu, 04 Jul 2019, 15:58:56 EST

Every reasonable effort has been made to ensure that permission has been obtained for items included in DRO. If you believe that your rights have been infringed by this repository, please contact drosupport@deakin.edu.au.